I-Yttrium yazinza ubuhlalu bokugaya be-zirconia | |
Amanyanjana | I-YSZ ubuhlalu (imidiya yokugaya) |
Case No. | 308076-80-4 |
Ifomula ye-Linear: | Y2o3 • ZRO2 |
I-Elastic modulus: | 200 gpa |
Ukuvuselelwa okushisayo: | 3 w / mk |
Ukuchoboza umthwalo: | ~ 20 kn |
Ukuqina kwe-Fracture: | 9 MPA * m1-2 |
I-YTTRIUM EZIQINISEKISA I-ZIRCONIA BRICKING Ubuhlalu
Izingxenye eziphambili | Ubuningi Bangempela | Ubuningi obuningi | Ubulukhuni bukaMoh | Ukuphakamayo | Amandla acindezelayo |
I-ZRO2: 94.6% Y2o3: 5.2% | I-6.0g / cm3 | 3.8g / cm3 | 9 | <20ppm / hr (24hr) | > 2000kn (Φ2.0mm) |
0.1-0.2mm 0.2-0.3mm 0.3-0.4mm 0.4-0.6mm 0.6-0.8mm 0.8-1.2mm 1.0-1.2mm1.2-1.4mm 1.4-1.6mm 1.6-1.8mm 1.8-2.0mm 2.0-2.2mm 2.2-2.6mm2.6-2.8mm 2.8-3.0mm 3.0-3.5mm 3.5-4.0mm 4.0-4.5mm 4.0-5.5mm 5.0-5.5mm 5.0-5.5mm5.5-6.0mm 6.0-6.5mm 6.5-7.0mm Abanye osayizi bangatholakala ngokususelwa kwisicelo samakhasimende |
Ukupakisha insizakalo: Hlela ngokucophelela ukunciphisa ukulimala ngesikhathi sokugcina nokuhamba kanye nokugcina ikhwalithi yemikhiqizo yethu esesimweni sabo sokuqala.
Yini i-ytttrium eqinisi ubuhlalu obudidiyela bokugaya?
I-YTTRIUM EZIQINISEKILE ZIRCONIA ubuhlalu yimidiya ehlala isikhathi eside futhi esebenza kahle kakhulu yokugaya kwebhola kanye nokulanda ukugaywa kwezinto zokwenziwa kwe-ceramic. I-Zirconia yokugaya imidiya ingasetshenziswa ezinhlobonhlobo zezicelo ezifana ne-nanostrupture kanye ne-superfine powders, inks, idayi, ukupenda nokupenda kobunzima, ama-ceramics asuselwa ku-chrome, kanye nezicelo zendwangu. Iphinde isetshenziselwe imishini yokugaya, ukudla, imithi nemithi nezinye izimboni ezikhethekile zamakhemikhali.