I-Manganese (ll, lll) i-oxide

Inkcazo emfutshane:

I-Manganese (II, III) I-oxide yi-oxide ingenamthombo we-manganese onsule, ehambelana nefomula ye-formula mn3o4. Njengesifo sentsimbi ye-ox, i-trimanganese ttiraoxide mn3o inokuchazwa njenge-MNo.mn2o3, kubandakanya amanqanaba amabini e-oxidation ye-MN2 + ne-MNN Ingasetyenziselwa izicelo ezahlukeneyo ezinjenge-Cataissis, izixhobo ze-electromic, kunye nezinye iinkqubo zokugcina amandla. Ikwalungele iglasi, izicelo ze-optic kunye ne-ceramic.


Iinkcukacha zemveliso

I-Manganese (II, II) I-Oxide

Izithethantonye I-Manganese (II) Dimanganese (III) Oxide, i-manganese Tetroxide, iManganese Oxide, iManganemaneXanguc Axide, i-trimanganese Tetraxide, Trimanganese Tetroxide
I-CASS No. 1317-35-7
Ifomula yekhemikhali Mn3o4, mno · mn2o3
Ubunzima be-molar 228.812 g / mol
Imbonakalo umgubo omnyama
Ukuxinana 4.86 g / cm3
Indawo yokunyibilika I-1,567 ° C (2,853 ° F; i-1,840 k)
Indawo yokubila I-2,847 ° C (5,157 ° F; 3,120 k)
Ukunyibilikisa emanzini i-infline
Ukunyibilikisa Inyibilikisiwe kwi-HCL
Imagnethices + 4500 · 10-6 cm3 / mol

Ukuchazwa kweshishini kwi-manganese (II, III) I-oxide

Isimboli Icandelo lemichiza I-Gariality (μm) I-TAPINIT (G / CM3) Indawo ethile yomphezulu (M2 / g) Isixhobo semagnethi (i-PPM)
Mn3o4o4 ≥ (%) Mn ≥ (%) I-Mat yeHlabathi. ≤%
Fe Zn Mg Ca Pb K Na Cu Cl S H2o
Ummo70 97.2 70 0.005 0.001 I-0.05 I-0.05 I-0.01 I-0.01 I-0.02 I-0.0001 0.005 I-0.15 0.5 I-D10≥3.0 D50 = 7.0-11.0 D100≤25.0 ≥2.3 ≤5.0 ≤0.30
Ummo69 95.8 69 0.005 0.001 I-0.05 I-0.08 I-0.01 I-0.01 I-0.02 I-0.0001 0.005 I-0.35 0.5 I-D10≥3.0 D50 = 5.0-10.0 D100≤30.0 ≥2.25 ≤5.0 ≤0.30

Singakwazi nokuthumela ezinye iinkcukacha, ezinjengeManganese Assay of i-65%, i-67%, kunye ne-71%.

Yintoni iManganese (II, III) i-oxide isetyenziselwe? I-MN3O4 ngamanye amaxesha isetyenziswa njengezinto zokuqala kwimveliso ye-Ferrites ethambileyo, umz. I-Manganese Tetroxide inokusetyenziswa njengearhente enobunzima ngelixa iqhuba amacandelo endawo yokugcina i-oyile kunye negesi yegesi. I-Manganese (III) AXCID ikwasetyenziselwa ukuvelisa iimagnethi ze-ceramic kunye ne-semicondtors.