Nickel(II) pulveris oxydi (Ni Assay Min.78%) CAS 1313-99-1
Nickel(II) Oxide
| Synonym: | Nickel Monoxidum, Oxonickel |
| CAS NO: | 1313-99-1 |
| Formulae chemica | NiO |
| Molar massa | 74.6928g/mol |
| Aspectus | viridi crystallinum solidum |
| Densitas | 6.67g/cm3 |
| punctum liquescens | 1,955°C(3,551°F; 2,228K) |
| Solubilitas in aqua | insensibilis |
| Solubilitas | dissolvere in KCN * |
| Susceptibilitas magnetica (χ) | +660.0·10−6cm3/mol |
| Index refractivus (nD) | 2.1818 |
Inceptum Specificationis pro Nickel(II) Oxide
| Symbolum | Nickel ≥(%) | Peregrinatio, Matth. ≤ (%) | |||||||||||
| Co | Cu | Fe | Zn | S | Cd | Mn | Ca | Mg | Na | Insolubilis Hydrochloricacid(%) | Particula | ||
| UMNO780 | 78.0 | 0.03 | 0.02 | 0.02 | - | 0.005 | - | 0.005 | - | - | D50 Max.10μm | ||
| UMNO765 | 76.5 | 0.15 | 0.05 | 0.10 | 0.05 | 0.03 | 0.001 | - | 1.0 | 0.2 | 0.154mm pondus screenresiduumMax.0.02% | ||
Sarcina: In situla stipata et intus conglutinatione ethene signata, pondus rete est 25 chiliogramma per situlam;
Quid est Nickel (II) Oxide adhibitum?
Nickel (II) Oxide adhiberi potest ad varias applicationes speciales et generaliter, applicationes distinguunt inter "gradum chemicum", quod est relative pura materia applicationis specialitatis et "gradus metallicus", quae maxime adhibentur ad mixtorum productionem. In ceramica industria adhibetur ad fricta, ferrites, ac fictilem glazeam. Oxide sintered adhibita ad mixturas chalybeas producendas. Solet est insolubilis in solutionibus aqueis (aquarum) et valde stabilis, utilia in structuris ceramicis efficiens tam simplex quam argillas ad electronicas provectas producens ac leve pondus structurarum partium in applicationibus aerospace et electrochemicis, sicut cibus cellulis in quibus ionicis conductivity exhibent. Nickel Monoxide saepe reflectitur cum acidis ad formandum sales (id est sulfamatus nickel), quae valent ad electroplates et semiconductores producendos. NiO communis usus est foraminis onerariis materiae in tenuibus cellulis cinematographicis solaris. Nuper NiO adhibitum est ut gravidae NiCd rechargebiles in multis electronicis machinis inventae sint donec evolutionem in altilium environmentally- NiMH superiorem. NiO materia electrochromica anodica, late investigata est ut electrodes occurro cum oxydatu, materia electronico-cathodica, in machinis electrochromicis complementariis.